That's not been my experience.
I haven't seen any whiskers on solder, but since I look I often see
them on plated metal parts (relay housings, shielding boxes, brackets,
switches, etc.) and also some components leads of ICs and such.
This has always been in very old equipment 30 years+, well pre-ROHS. I
have never found whiskers in modern or leadfree soldered equipment
myself, but don't doubt others might have.
Perhaps it is just that the old whiskers are much longer, and can be
spotted with the naked eye, but I have always considered this a legacy
problem from before they knew to avoid bright tin plating. I think in
many situations they would just burn away, they are very thin.
From what I understand it's mostly the bright (pure) tin plating
that's the problem, and most alloy solders are fine, even if it is
just small amounts mixed in. It's also a factor how thick the plating
is (galvanic or hot dipped) but don't recall which is worse.
ST
On Sun, Jul 31, 2016 at 12:35 AM, Harvey White
madyn@... > From what I know, regular tin plating is not a problem. Mostly tin
> solder is. How long this whisker growth takes I do not know, a rough
> suspicion (and that's all it is) says 3 to 5 years regardless of what
> you do.