> Questions:
> 1. Should the whole board come out with really god adhesion?
yes. only sometimes on the edges i had a bad spot (i have a board outline
trace most time which likes to get off where i start peeling the paper)
> 2. Any ideas? Is this a pressure issue (I left the iron and steel plate
> with
> no pressure)?
I apply pressure, no idea, maybe 30N or so.. no more than 60N.
> Temp issue (the paper turned brown after being under the iron
> for a short time, the copper oxidized where it was not under the paper)?
My paper gets slightly brown (more yellow) after the whole run. the copper
discolors very slightly too.
> Time (8 min)?
>
30 second to 1 minute.
may be too long your 8 minutes.
you can cut down time if you preheat the board but i don't really see a
reason.
> Thanks for the help I am definitely farther than I have ever been.
> John
>
not sure if you steel plate is perfect, i don't really get the picture, do
you attach the steel plate to the iron and press with it or what?
st