You can put more copper oxide to increase etch rate. From memory
I think its around 140 g/L of copper(II) ions is good concentration.
What copper oxide did you get, the black stuff or red ?
Black is more common which is copper(II) oxide.
100 g copper(II) oxide (black) = 66g copper
100 g copper(I) oxide (red) = 89g copper
Les Newell wrote:
> My chemicals finally arrived today so I made up a batch of cupric
> chloride etchant. The ingredients I used were:
>
> 250g copper oxide
> 790 ml 35% hydrochloric acid. This is probably not as accurate as going
> by weight but there is no way I am letting that stuff near the kitchen
> scales :-)
> enough water to make up 2.5 litres
>
> I added the acid to about 1 litre of water a little at a time, stirring
> all the time. Once all the acid was in the solution reached 30 deg
> centigrade, from 13 deg C when I started. I then added the copper oxide
> and stirred well. I dumped the whole lot into a 2.5 litre container and
> topped it up with water.
>
> The end result was a fairly deep green solution. In my etch tank at 35
> deg C it took 20 minutes to etch a board which seems slightly slower
> than new ferric but a lot quicker then the manky old ferric I was using
> :-) It does not seem to be as agressive as ferric. The board I used was
> an old board that was over exposed and has been lying around for about a
> year. Some areas took a while to start etching due to accumulated
> oxides, fingerprints etc. A piece of the same board dunked in ferric
> seemed to etch more evenly.
>
> 35% HCl is pretty nasty stuff. I mixed up the solution outdoors in
> fairly damp conditions and there were clouds of fumes coming from the
> container of acid.
>
> All I need to do is get the new light box sorted out and I will be able
> to try the etchant properly.
>
> Les
>
>
>
>
>
> Be sure to visit the group home and check for new Bookmarks and files:
> http://groups.yahoo.com/group/Homebrew_PCBs
>
> To unsubscribe from this group, send an email to:
> Homebrew_PCBs-unsubscribe@yahoogroups.com
>
>
>
> Your use of Yahoo! Groups is subject to http://docs.yahoo.com/info/terms/
>
>