> Put in lot more acid, make it like 100 g/L. Where are you
> getting the acid ?
> Solder will be ok for anode, but expect lots of black
> looking sludge to form as the lead sulfate formed is
> insoluble. Bagging the anode is a good idea.
>
> I assume you will be going to use alkaline ammonia etching
> as that's the only etchant compatible with tin metal resist.
>
> Below is the URL to the web page I wrote a long time go
> describing the procedure for preparing a acid tin sulfate
> plating baths.
>
> http://members.optusnet.com.au/~eseychell/electrolyte.html
>
>