I'm using 30% H2O2, not 3%, but I have to do some calculations to
compare the two.
Mark
At 05:11 PM 3/18/2010, you wrote:
>Mark, I am a long way from being an expert, but until one of the
>experts chips in, I'll say that the proportions don't sound right to
>me. I use 1 part 30% HCl, and 2 parts 3% H2O2, and it etches
>quickly. So it would seem that you are using a way, way higher
>concentration of H2O2 to HCL -- ??
>
>FWIW, even though this mixture etches quickly, it does etch from the
>outside edges in -- but that is true of every etching I have seen or
>done, not that that is a very large sample.
>
>--- In Homebrew_PCBs@yahoogroups.com, Mark Lerman <mlerman@...> wrote:
> >
> > It's Claroxide 30, from a beauty supply, and should be fresh. Perhaps
> > I'm using too little - I used 30 cc water +30cc HCl +10cc H2O2 for a
> > ds board that measured about 4x2 inches. I don't know the thickness
> > of the copper. The board was etched horizontal in a container with
> > the etchant level only about .25 inches above the surface of the board.
> >
> > Mark
> > \
> > At 12:35 PM 3/18/2010, you wrote:
> > >Is the H2O2 fresh? It breaks down over time, a solution that's been
> > >mixed for a while won't have any H2O2 left in it, and HCl won't etch Cu
> > >without an oxidizer.
> > >
> > >Are you sure you used 30% H2O2 and not the more common 3% ?
> > >
> > >
> > >------------------------------------
> > >
> > >Be sure to visit the group home and check for new Links, Files,
> and Photos:
> > >http://groups.yahoo.com/group/Homebrew_PCBsYahoo! Groups Links
> > >
> > >
> > >
> >
>
>
>
>
>------------------------------------
>
>Be sure to visit the group home and check for new Links, Files, and Photos:
>http://groups.yahoo.com/group/Homebrew_PCBsYahoo! Groups Links
>
>
>